牌號 | 化學成分(質量分數)(%) | ||||
C | Si | Mn | Cr | 其 他 | |
ML08 | 0.05~0.12 | ≤0.03 | O.20~0.50 | O.7~1.0 | |
MLlO | 0.07~O.14 | ||||
MLl5 | O.12~O.19 | ≤0.07 | |||
M120 | 0.17~0.24 | ||||
ML25 | 0.22~O.30 | ≤O.20 | 0.30~O.60 | ||
ML30 | O.27~O.35 | ||||
ML35 | 0.32~O.40 | ||||
ML40 | O.37~0.45 | ||||
ML45 | 0.42~0.50 | ||||
ML2SMn | 0.22~O.30 | ≤0.25 | 0.50~O.80 | ||
MIJ30Mn | O.27~0.35 | ||||
ML35Mn | O.32~0.40 O.37~O.45 | ||||
ML40Mn | |||||
ML45Mn | O.42~O.50 | ||||
MLl5Cr | O.12~O.18 | ≤0.30 | 0.40~O.70 | ||
ML20Cr | O.17~0.24 | O.50~O.80 | |||
ML40Cr | 0.37~0.44 | O.80~1.10 | |||
MLl5MnB | O.14~O.20 | 1.20~1.60 | BO.0005~O.0035 | ||
MLl5MnVB | O.12~0.18 | V0.07~O.12 BO.0005~0.0035 | |||
ML20MnT-B | O.17~O.24 | 1.30~1.60 | BO.0005~0.0035 TjO.04~O.10 | ||
M100CrMo | O.26~O.34 | 0.40~0.70 | O.80~1.10 | Mo0.15~0.25 | |
ML35CrMo | 0.32~0.40 | O.40~O.70 | |||
ML42CrM0 | 0.38~0.45 | O.50~0.80 | O.90~1.20 |
牌號 | 抗拉強度 ób | 屈服點ós | 伸長率ó5 | 斷面收縮率Ψ | 衝擊韌度a k | 硬 度 | |||||
熱軋 | 退火 | ||||||||||
MPa | % | J/cm² | 壓痕直徑 /mm | 布氏硬度 HBS | 壓痕直徑 /mm | 布氏硬度 HBS | |||||
≥ | ≥ | ≤ | ≥ | ≤ | |||||||
ML08 | 334 | 196 | 33 | 60 | 5.2 | 131 | |||||
MLl0 | 333 | 206 | 3l | 55 | 5.1 | 137 | |||||
MLl5 | 377 | 226 | 27 | 55 | 5.0 | 1,13 | |||||
ML20 | 412 | 245 | 25 | 55 | 4.8 | 156 | |||||
M125 | 451 | 275 | 23 | 50 | 4.6 | 170 | |||||
ML30 | 490 | 296 | 2l | 50 | 4.5 | 179 | |||||
M135 | 530 | 314 | 20 | 45 | 4.4 | 187 | |||||
ML40 | 569 | 333 | 19 | 45 | 4.1 | 217 | 4.4 | 187 | |||
ML45 | 598 | 353 | 16 | 40 | 4.0 | 229 | 4.3 | 197 | |||
ML25Mn | 451 | 275 | 23 | 50 | 4.6 | 170 | |||||
ML30Mn | 490 | 294 | 21 | 50 | 4.5 | 179 | |||||
ML35Mn | 530 | 314 | 20 | 45 | 4.4 | 187 | |||||
ML40Mn | 569 | 333 | 19 | 45 | 4.1 | 217 | 4.4 | 187 | |||
ML45Mn | 598 | 353 | 16 | 40 | 4.0 | 229 | 4.3 | 197 | |||
MLl5Cr | 686 | 490 | lO | 45 | 69 | 4.5 | 179 | ||||
ML20Cr | 785 | 588 | lO | 40 | 59 | ||||||
ML4OCr | 981 | 785 | 9 | 45 | 59 | 4.2 | 207 | ||||
MLl5MnB | 1128 | 932 | 9 | 69 | |||||||
MLl5MnVB | 1079 | 883 | 10 | 4.2 | 207 | ||||||
ML20MnTiB | 1128 | 932 | 4.4 | 187 | |||||||
M130CrMo | 932 | 785 | 12 | 50 | 78 | 4.0 | 229 | ||||
M135CrMo | 981 | 834 | 45 | ||||||||
ML42CrMo | 1079 | 932 | 4.1 | 217 |
牌 號 | 試樣熱處理制度 |
ML08、MLlO、MLl5、ML20、ML25、 ML30、ML35、ML40、ML45、ML25Mn、ML30Mn、ML35Mn、ML4OMn、ML45Mn | 加熱到高於臨界點30~50℃,保溫30min以上,空冷 |
MLl5Cr、ML20Cr | 一次淬火880℃, 二次淬火800℃,水、油冷,回火200℃,水、空冷 |
ML40Cr | 淬火850℃,油冷,回火520℃,水、油冷 |
MLl5MnB | 淬火880℃,水冷,回火200℃,水、空冷 |
MLl5MnVB | 淬火880℃,油冷,回火200℃,水、空冷 |
ML20MnTiE | 淬火860℃,油冷,回火200℃,水、空冷 |
ML30CrMo | 淬火880℃,水、油冷,回火540℃,水、油冷 |
ML35CrMo | 淬火850℃,油冷,回火550℃,水、油冷 |
ML42CrMo | 淬火850℃,油冷,回火560℃,水、油冷 |