簡介
| 指標名稱 | 指標 |
| 外觀 | 乳白或淡黃色不透明球狀顆粒 |
| 出廠型式 | 游離胺型 |
| 含水量 % | 48.00-58.00 |
| 質量全交換容量 mmol/g | ≥4.80 |
| 強型基團容量 mmol/g | ≤1.00 |
| 體積全交換容量 mmol/ml | ≥1.45 |
| 濕視密度 g/ml | 0.65-0.72 |
| 濕真密度 g/ml | 1.030-1.060 |
| 範圍粒度 % | (0.315-1.25mm)≥95 |
| 上限粒度 % | (>1.25mm)≤1 |
| 有效粒徑 mm | 0.50-0.700 |
| 均一係數 | ≤1.60 |
| 滲磨圓球率 % | ≥90.00 |
用途
主要用於純水及高純水製備，電鍍含鉻廢水處理等其他相關
研究了酸性條件下氯酚在大孔弱鹼樹脂D301上的吸附機理。研究表明,在一定的吸附質濃度及pH值下, D301樹脂對對氯酚和鄰氯酚的吸附量與溶液平衡濃度之間存在良好的線性關係,吸附過程類似於固相萃取過程,且分配係數與相應pH值下X射線光電子能譜(XPS)測得的樹脂上自由叔胺基團含量呈線性關係。In the present study X-ray photoelectron spectroscopy (XPS) was adopted to elucidate sorption mechanism of o-chlorophenol and p-chlorophenol onto a weak anion exchanger D301. The distribution of specific forms of amino groups on D301 was obtained and effect of free tertiary amine group on phenol sorption onto D301 was discussed. The result indicate that less free amino group on D301 caused by external solution with lower pH leads to less sorptive capacity of o-chlorophenol and p-chlorophenol respectively. U...
| 文獻名稱 | 氯酚在D301樹脂上吸附機理的研究 |
| Article Name 英文（英語）翻譯 | STUDY OF SORPTION MECHANISM OF o-CHLOROPHENOLAND p-CHLOROPHENOL ONTO D301; |
| 作者 | 李曉弢； 潘丙才； 孟凡偉； 陳新慶； 潘丙軍； 陳金龍； |
| Author | LI Xiaotao PAN Bingcai MENG Fanwei CHEN Xinqing PAN Bingjun CHEN Jinlong State Key Laboratory of Pollution Control and Resources Reuse School of the Environment;Nanjing University;Nanjing 210093;China; |
| 作者單位 Author Agencies | 污染控制與資源化研究國家重點實驗室； 南京大學環境學院； 南京大學環境學院 南京； |
| 文獻出處 Article From | 離子交換與吸附；Ion Exchange and Adsorption;2005年 03期； |
| 關鍵字 | 氯酚； 吸附機理； D301樹脂； XPS; pH值； |
| Keywords | chlorophenol;sorption mechanism;weak anion exchanger D301;XPS;pH.; |