耐蝕合金冷軋帶(GB/T15012
(1)尺寸規格見表8-52。表8-52耐熱合金冷軋帶的尺寸規格 (mm) 厚度及 厚度允 許偏差 | 寬度 厚度 | 厚度答應偏差 |
20~150 | >150~250 | >250~400 | >400~630 |
0.02~O.10 | ±O.008 | ±O.010 | ±O.OlO | |
>0.10~0.15 | ±0.010 | ±0.010 | ±O.OlO | |
>O.15~O.25 | ±O.015 | ±0.015 | ±O.015 | ±0.020 |
>O.25~O.45 | ±O.020 | ±0.020 | ±O.020 | ±O.025 |
>O.45~0.65 | ±O.O25 | ±0.025 | ±0.025 | ±O.030 |
>O.65~O.90 | ±O.030 | ±0.030 | ±0.030 | ±0.040 |
>0.90~1.20 | ±0.035 | ±O.040 | ±O.040 | ±O.045 |
>1.20~1.50 | ±O.045 | ±O.050 | ±O.050 | ±O.055 |
>1.50~1.80 | ±0.06 | ±0.065 | ±0.065 | ±O.07 |
>1.80~2.00 | ±O.06 | ±0.07 | ±0.075 | ±O.08 |
>2.00~2.30 | ±O.07 | 士O.08 | ±0.08 | 士0.09 |
>2.30~2.50 | ±O.07 | 土O.08 | ±0.08 | ±0.09 |
>2.50~3.10 | ±O.08 | ±O.09 | ±O.09 | ±O.10 |
>3.10~4.00 | ±O.09 | ±O.10 | ±O.10 | ±0.11 |
寬度及寬度允 許偏差 | 寬度邊沿狀態 | 寬度答應偏差 |
20~50 | >50~150 | >150~250 | >250~400 | >400~630 |
切邊帶材 | +l.O O | +2.O O | +3.0 0 | +4.0 0 | +5.0 0 |
不切邊帶材 | +2 -l | +3 -2 | +6 -2 | +7 -3 | +20 O |
註:1.切邊帶材的鐮刀彎應符合下列規定: 寬度20—50mm帶材,每米長度不大於3mm;寬度大於50mm帶材,每米長度不大於2mm。 2.根據需方要求,可以把表中厚度的正負偏差改為正偏差或負偏差,但此時的公差值應與表中規定的公差值相等。(2)力學性能見表8-53。表8-53耐蝕合金冷軋帶的力學性能 合金牌號 | 狀態 | 抗拉強度ób/MPa | 屈服強度ó0.2/MPa | 伸長率δ5(%) | 硬度 |
≥ |
NS111 NS112 | 退火 | 520 | 205 | 30 | — |
ns142 | 退火 | 585 | 240 | 30 | ≤95HRB |
NS311 | 固溶 | 570 | 245 | 45 | — |
1/2H | 805 | — | 10 | — |
NS312 NS315 | 退火 | 505 | 240 | 30 | — |
1/4H | — | — | — | 88~94HRB |
1/2H | — | — | — | 93~98HRB |
3/4H | — | — | — | 97HRB~25HRC |
H | 860 | 620 | 2 | — |
NS321 | 退火 | 795 | 345 | 45 | 100HRB ① |
NS322 | 退火 | 760 | 350 | 40 | 100HRB ① |
NS333 | 固溶 | 690 | 315 | 30 | — |
NS336 | 退火 | 830 | 415 | 30 | — |
固溶 | 690 | 275 | 30 | — |
註:1.屈服強度值,僅當需方要求時(在契約中註明)才測定。 2.屈服強度要求不適用於厚度小於0.50mm的帶材。 3.厚度小於0.25mm的帶材不作拉力試驗,但應提供硬度數據。①硬度值僅供參考。 ![聯絡我們 聯絡我們](/contactus.png)